Name. | Ready to press powder | |||||||||||||
Desc. | White powders | |||||||||||||
Tightly sealed with plastic film in PP drum. | ||||||||||||||
App. | Compared with other manufacturers, SZ-SB-3.0 been produced with the advantages of low sintering temperature, white, good transparent and high batch consistency. It is widely been used in zirconia ceramic beads, sand mill accessories, bearing sleeve and other industry parts. The newly developed SZ-FS-B further improves the pressing performance, strength and toughness, and can be widely used in applications requiring higher strength and toughness, such as ceramic measuring tools and ceramic plunger industries. | | ||||||||||||
Spec. | Grade | ZrO2(HfO2)+Y2O3 | Al2O3 | Cl- | Fe2O3 | BET | D50 | |||||||
SIZE-YSZ-SB | ≥99wt% | <5000ppm | ≤200ppm | ≤50ppm | 9-11m2/g | 0.6-1.0μm | ||||||||
SZ-SB-3.0 | ≥99wt% | <2500ppm | ≤200ppm | ≤50ppm | 10-12m2/g | 1.2-1.8μm | ||||||||
Other impurities such as Si, Fe, Na, Al are controlled below 100ppm; | ||||||||||||||
Suggesting forming method | un-axial and CIP | |||||||||||||
Typical Flexural strength | >800MPa | |||||||||||||
Suggesting firing temperature | 1450-1550℃ | |||||||||||||
Typical firing density | ≥6.0g/cm3 | |||||||||||||
For more information please contact our professional sellers. | ||||||||||||||
Photos. |
SEM of Sintered sample |
SEM of Sintered sample | ||||||||||||
Remark. | Information showed above only for reference, prevail with the agreed quality standards after sale. Carefully read the MSDS document before using; Process performance may not be suitable for some specific circumstances, please contact our company professional guidance; Product can be customized according to customer specific requirements. |